Qingdao IC-2005 high temperature pure manganese phosphating liquid

IC-2005 is a high-temperature manganese-based phosphating agent, suitable for self-lubricating coating processing of high-speed running parts of automobiles, motorcycles, and shipbuilding, as well as wear-resistant and corrosion-resistant coating processing of tools, cutters, and higher-standard parts. Phosphating liquid can form a dense, wear-resistant black phosphating film on the surface of steel. The phosphating film is composed of a series of crystals of different sizes. The connection points of the crystals form a porous structure with tiny cracks. The porous crystal structure can significantly improve the corrosion resistance, adsorption and wear resistance of the steel surface in a lubricating oil or anti-rust oil environment.

1. Oil and rust removal must be thorough. If the effect of adding the phosphate film is not satisfactory, the workpiece can be immersed in a pickling tank to remove the phosphate film (it must be removed completely), and then re-coated with phosphate.

2. The washed workpiece cannot be left in the air for too long to prevent rust, and the water in the cleaning tank should flow to ensure the quality of the water.

3. Test TA and FA twice a day.

4. After washing, the phosphated workpiece should be dried at 100 to 150 degrees to increase the corrosion resistance. Natural drying is not a good method.

Packaging: 25kg/barrel, 200kg/barrel

Storage: Store in a cool, dry place, avoid direct sunlight and contact with alkaline substances.