Refractory Brick Pizza Oven Refractory Brick Oven Brick Manufacturer

Product Detail

Silica content (%):custom madebrand:Shuo Jin
Advantage:insulation, fire protection,Refractoriness/°C:1580~1770
product name:Clay refractory brickRefractoriness (degrees):Ordinary (1580°
usage:kiln masonry materialsBulk density g/cm3:2.15-2.3
Packaging Details:Packing instructions 1 pallet + plastic film + fixing belt 2 pallets: 1*1m, 0.93*0.93m 3 pallets Weight: 1.6~2.0 tons 4 According to customer service packagingSilicon carbide content (%):custom made
Raw materials:clay clinkerCaO content (%):custom made
shape:brickcolor:Red
payment terms:L/C, Western Union, D/P, D/A, T/T, MoneyGramProcessing services:Bending, punching, cutting, forming
Al2O3 content (%):48%Package preview:
application:Furnace liningtype:refractory
size:230x114x65mmmodel:SK-35
Supply capacity:100,000 kg per monthCrO content (%):custom made
port:Qingdao Port;Material:clay
place of origin; place of origin:Henan, ChinaMgO content (%):custom made
Application of refractory clay brick
One.Clay refractory bricks for blast furnaces are clay bricks used for blast furnace linings made of refractory clay. Clay refractory bricks for blast furnaces are used in throats, shafts, hearths, bottom linings of small blast furnaces and shafts of large blast furnaces.
b.Clay bricks for hot blast stoves are made of refractory clay and are used to build clay bricks for blast furnaces. Clay bricks for hot blast stoves are used for hot blast stoves, regenerators and partition walls. Clay bricks for hot blast stoves require good thermal shock resistance, high load softening temperature and low creep.
c.Large-size clay refractory bricks for glass kilns are clay refractory bricks with a unit weight of not less than 50kg for masonry glass kilns.
Model
content
LZ-48
LZ-55
LZ-65
LZ-75
Alumina content
48%≧
55%≧
65%≧
75%≧
Iron oxide content
2.0%<
2.6%<
2.5%<
2.5%<
Bulk density
2.0g/㎡
2.3g/㎡
2.4g/㎡
2.5g/㎡
Compressive strength at room temperature
39.2mpa>
50mpa>
60mpa>
70mpa>
load softening temperature
1420°C
1420°C
1460°C
1510°C
Refractory temperature
1750°C
1770°C
1770°C
1790°C
Apparent porosity
22%<
24%<
23%<
22%<
linear rate of change
-0.2%
-0.4%
-0.4%
-0.3%
VIEW MORE