230x114x65MM size refractory interlocking clay refractory bricks for kiln

Product Detail

brand:LecterHigh temperature cone equivalent Orton cone:31-32
Package preview:Al2O3 content (%):36.2
Titanium dioxide(%):3Bulk density (kg/m3):2100-2200
port:QingdaoNa2O+K2O+Li2O(%):0.5
Material:flint clayApparent porosity(%):22-24
Refractoriness (degrees):Ordinary (1580°Supply capacity:2,000,000 kg per month
CaO content (%):0.5payment terms:L/C, Western Union, T/T, Paypal
Packaging Details:Trays with stretch filmOrigin:Shandong Province, China
Modulus of rupture (kg/cm2):55-70Magnesium oxide content (%):/
Cr2O content (%):/Silicon carbide content (%):/
Processing services:cutting, formingSodium oxide (%):0.6
Ferric oxide(%):2Silica content (%):57.8
Cold crushing strength (MPa):22-32model:SK32
shape:brick

230x114x65MM size refractory interlocking clay refractory bricks for kiln

RonkettSupply a full range of clay refractory bricks. Alumina content around 28-45% is classified as clay refractory brick

 

The main application is Clay refractory brickListed below:

• Furnace construction

• Blast Furnace/Hot Stove

• Steel foundries

• Furnace for non-ferrous metal industry

• Coke and gas ovens

• Glass industry

• Cement industry

• Ladle safety lining

• Boiler spare lining

Product Description

Note: Special-shaped clay refractory bricks are more expensive than ordinary square or rectangular refractory bricks.

Clay Refractory Brick Product Data

Material Common special
blast furnace Hot stove glass furnace
thing SK32 SK34 ZGN-42 GN-42 RN-42 RN-40 RN-36 BN-40a BN-40b

High temperature cone equivalent

orton cone

31-32 33-34
Refractoriness (°C) 1715 1760 1760 1760 1760 1740 1700
Bulk density (kg/m3) 2100-2200 2200-2250 2200 2200 2200 2200 2150 2250 2250
Apparent porosity(%) 22-24 18-20 days ≤15 ≤16 ≤24 ≤24 ≤25 ≤18 ≤18
Cold crushing strength (MPa) 22-32 30-35 ≥58.8 ≥49.0 ≥29.4 ≥24.5 ≥19.6 ≥49.0 ≥34.3
Modulus of rupture (kg/cm2) 55-70 60-80

reheat test,

Everlasting

linear change

after heating

(1350℃%, 3h) 0~-3 0~-0.5    
(1400℃%, ​​2h) 0~-0.4 0~-0.4
(1450℃%, 3h) 0~-2 0~-3 0~-0.4
(1400℃%) 0.0-0.2 -0.18
0.2MPa soft load (%) ≥1450 ≥1430 ≥1400 ≥1350 ≥1300 ≥1450 ≥1400
Silica (%) 57.8 52.4
Aluminum oxide(%) 36.2 42.1 ≥42 ≥42 ≥42 ≥40 ≥36 ≥40 ≥40
Ferric oxide(%) 2 1.4 ≤1.7 ≤1.7 ≤1.5 ≤1.5
Cao (%) 0.5 0.4
Na2O+K2O+Li2O (%) 0.5 0.5