Stainless steel aluminum copper alloy environmental protection metal degreaser oil cleaner 10500

a. Excellent penetration and wetting ability, providing super degreasing power. Low-foaming, fast-dissolving, no-rinse, no-coagulation restrictions. Biodegradable properties promote easier rinsing.

b. Non-phosphate products run at room temperature. Suitable for stubborn oil stains, rust and oil removal on all hard surfaces, especially for high-precision base parts without corrosion problems. Commonly used in rack plating, barrel plating, continuous plating lines and vibrating machines.

c. It is suitable for acid and alkali systems, suitable for cleaning all metal and non-metal surfaces, especially precision copper parts, and removing stubborn oil stains and hard films.

 2. Operating Instructions

Iron: Use 10500 10%, combined with sodium hydroxide 2-5g/L to quickly remove stubborn oil film and dirt. For iron with slight rust, it is appropriate to use 10% 10500 and 10-40% hydrochloric acid. When used in conjunction with a vibrating machine, use 10500 1Kg, sodium hydroxide 1-2Kg.

Copper sheet: 10500 10%, 1-3g/L sodium hydroxide can also be used appropriately, which can enhance more emulsifying power for heavy oil and grease. Add in a 50:1 ratio. For high-precision parts, adding sodium hydroxide is not recommended. Acidic copper plating process: 10500 2-3%, can quickly remove the organic film and dye particles attached to the copper plating surface, reduce the roughness of the plating layer and increase the brightness of the plating layer. It can also prevent the oxidation of the copper layer caused by the long time in the air on the automatic electroplating line, which will affect the performance and appearance of the subsequent plating layer.

Zinc, aluminum alloy: 10500 3-5%, can quickly remove the oxidized oil film on the surface. For the vibrating machine, it is appropriate to use 1Kg of sodium silicate or trisodium phosphate, and 1Kg of 10500,

Electrophoresis process: 10500 3-5%, which can quickly remove the oxidized oil film on the metal surface and enhance the adhesion of electrophoresis.

ABS plastic plating: 10500 3-5% Used for degreasing before roughening of chrome plating. It can replace the hydrophilic agent, and can also solve the skip plating problem of chrome roughening in the concave part.

 3. Running time: 1-8 minutes at room temperature.