HK-2000 Jewelry Foundry Investment Powder

Product Detail

Origin:Guangdong, Chinause:9~18k Gold Silver Beryllium Copper Embedding Powder
model:HK-2000shape:powder
size:22.5kg/bagMaximum burning temperature:750 (1,382°F)
raw material:plastertype:slaked lime
payment terms:wire transfersize:22.5kg/bag
Name:HK-2000 Jewelry Foundry Investment PowderModel:HK-2000
brand:hunterfor:Jewelry Investment Casting
MOQ:20 tonssize:22.5kg/bag
Supply capacity:45000 kg per monthbrand:hunter
nation:China
  • feature:
    1
    The casting mold can withstand the temperature of 720oC (1328oF) ~ 750oC (1382oF), and has high thermal shock resistance. Casting molds can withstand rapid and direct temperature rises without cavity rupture.
    2The cavity is reproduced very clearly without any male and female surfaces on the casting surface. The casting feels very smooth, and the finishing gold consumption is very low.
    3Prepare embedding with 3% boric acid, which can be directly used for in-situ wax setting of stone (diamond).
    4The embedding powder is suitable for high-end jewelry casting of pure gold, K gold, silver and brass alloy, and is a commonly used embedding material.
    5Automatic folding when immersed in water, easy to make patterns.

Model:

HK-2000

Water/powder ratio:

38-40:100

operating hours:

9-10 minutes

Initial setting time:

12-15 minutes

Thermal Expansion@730:

0.75%

Set extension @2hrs.:

0.50%

Hot pressing strength (730×1hrs):

0.69 MPa

Set compressive strength (2 hours):

1.27 MPa

Maximum burning temperature:

750 (1,382°F)

VIEW MORE